Fiber-reinforced thermoplastic resin molded article and fiber-reinforced thermoplastic resin molding material

A fiber reinforced thermoplastic resin molded article comprising (A) carbon fibers, (B) graphite and (C) a thermoplastic resin, wherein the carbon fibers (A), the graphite (B) and the thermoplastic resin (C) are contained in amounts of 1 to 30 parts by weight, 1 to 40 parts by weight and 30 to 98 parts by weight, respectively, relative to 100 parts by weight of the carbon fibers (A), the graphite (B) and the thermoplastic resin (C), weight average fiber length of the carbon fibers (A) is 0.3 to 3 mm and specific gravity of the molded article is 1.1 to 1.9 g/cm3,

• wherein the molded article comprises a skin layer, a core layer and a skin layer in this order as observed in the thickness direction, and the thickness of the core layer is 20 to 60% relative to the thickness of the molded article.