N-type doping of strained epitaxial germanium films through co-implantation and nanosecond pulsed laser melting

Abstract

In one aspect a method of fabricating an n-doped strained germanium (Ge) film is disclosed, which includes depositing a strained Ge film on an underlying substrate, implanting at least one electron-donating dopant in the Ge film, and exposing the implanted Ge film to one or more laser pulses having a pulsewidth in a range of about 1 ns to about 100 ms so as to generate a substantially crystalline strained Ge film. In some embodiments, the pulses can cause melting followed by substantial recrystallization of at least a portion of the implanted Ge film. In some embodiments, the resultant Ge film can have a thickness in a range of about 10 nm to about 1 microns.