Water-leachable alloy-melt-swapping process and porous metal manufactured using the same

Abstract

Disclosed is an AMS process using a water-leachable alloy that reacts with water and dissolves, and a porous metal manufactured using the same. An AMS precursor including element groups that are selected in consideration of the relationship of heat of mixing with the water-leachable alloy composition to be subjected to the AMS process is immersed in the alloy melt, thus manufacturing a bi-continuous structure alloy. The bi-continuous structure alloy is subjected to dealloying using water, thus manufacturing the porous metal. The water-leachable alloy is a Ca-based alloy having high reactivity to water and high oxidation resistance at high temperatures, and a dealloying process thereof is performed using only pure water, unlike a conventional dealloying process performed using a toxic etching solution of a strong acid/strong base. The metal porous body has high elongation, a large surface area, and low thermal conductivity.

Dependencies are inferred from the claim text.