Purified quartz powder modified for cladding optic fiber cable
AssigneeSibelco North America, Inc.
InventorsPaul Calderone, Brian Mosher, Chris Capobianco
Life of this patent
Estimating the term…
Abstract
A highly purified quartz powder having a low level of naturally occurring lithium modified for cladding a fiber optic cable, said modified quartz powder having an increased total amount of lithium in solid solution in said powder, said increased total amount being in the range of more than 0.50 ppm and less than 1.00 ppm and a method of modifying an highly purified quartz powder to make the same.
Claims8
A method of modifying a highly purified quartz powder having low level of naturally occurring lithium for use in cladding a fiber optic cable, said method comprising:
- a) forming a solution of a lithium doping agent;
- b) blending said highly purified quartz powder with said doping solution to provide a blended mass with a given level of lithium comprising lithium of said doping solution coated onto said highly purified quartz powder and the low level of naturally occurring lithium of said highly purified quartz powder, said blended mass having a moisture content of 2-5 percent;
- c) gassing said blended mass with a gas heated to a temperature of at least 1000° C. for a time to dope said highly purified powder with lithium in said doping solution;
- and,
- d) controlling the amount of lithium from said doping solution that is doped into said highly purified quartz powder so the total lithium in solid solution in said modified highly purified quartz powder is at a final level of 0.50-1.00 ppm.
A method of modifying a highly purified quartz powder having a low level of naturally occurring lithium for use in cladding a fiber optic cable, said method comprising:
- a) forming a solution of a lithium doping agent, which agent is a lithium salt, said salt being LiNO3;
- b) blending said highly purified quartz powder with said doping solution to provide a blended mass with a given level of lithium comprising lithium of said doping solution coated onto said highly purified quartz powder and the low level of naturally occurring lithium of said highly purified quartz powder;
- c) gassing said blended mass with a gas heated to a temperature of at least 1000° C. for a time to dope said highly purified powder with lithium in said doping solution;
- and,
- d) controlling the amount of lithium from said doping solution that is doped into said highly purified quartz powder so the total lithium in solid solution in said modified highly purified quartz powder is at a final level of 0.50-1.00 ppm.
A method of modifying a highly purified quartz powder having a low level of naturally occurring lithium for use in cladding a fiber optic cable, said method comprising:
- a) forming a solution of a lithium doping agent, wherein said doping agent includes aluminum to increase the portion of lithium from said blended mass converted to solid solution doped into said highly purified powder during said gassing operation, said agent being LiAlO2;
- b) blending said highly purified quartz powder with said doping solution to provide a blended mass with a given level of lithium comprising lithium of said doping coated onto said highly purified quartz and the low level of naturally occurring lithium of said highly purified quartz powder;
- c) gassing said blended mass with a gas heated to a temperature of at least 1000° C. for a time to dope said highly purified powder with lithium in said doping solution;
- and,
- d) controlling the amount of lithium from said doping solution that is doped into said highly purified quartz powder so the total lithium in solid solution in said modified highly purified quartz powder is at a final level of 0.50-1.00 ppm.
A method of modifying a highly purified quartz powder having a low level of naturally occurring lithium for use in cladding a fiber optic cable, said method comprising:
- a) forming a solution of a lithium doping agent, wherein the doping agent includes aluminum to increase the portion of lithium from said blended mass converted to solid solution doped into said highly purified powder during said gassing operation, wherein said doping agent is a lithium salt combined with aluminum salt, said agent being Al(NO)3;
- b) blending said highly purified quartz powder with said doping solution to provide a blended mass with a given level of lithium comprising lithium of said doping solution coated onto said highly purified quartz powder and the low level of naturally occurring lithium of said highly purified quartz powder;
- c) gassing said blended mass with a gas heated to a temperature of at least 1000° C. for a time to dope said highly purified powder with lithium in said doping solution;
- and,
- d) controlling the amount of lithium from said doping solution that is doped into said highly purified quartz powder so the total lithium in solid solution in said modified highly purified quartz powder is at a final level of 0.50-1.00 ppm.
A method of modifying a highly purified quartz powder having a low level of naturally occurring lithium for use in cladding a fiber optic cable, said method comprising:
- a) forming a solution of a lithium doping agent;
- b) blending said highly purified quartz powder with said doping solution to provide a blended mass with given level of lithium comprising lithium of said doping solution coated onto said highly purified quartz powder and the low level of naturally occurring lithium of said highly purified quartz powder and said given level of lithium being in the range of 0.80 to 2.0 ppm;
- c) gassing said blended mass with a gas heated to a temperature of at least 1000° C. for a time to dope said highly purified powder with lithium in said doping solution;
- and,
- d) controlling the amount of lithium from said doping solution that is doped into said highly purified quartz powder so the total lithium in solid solution in said modified highly purified quartz powder so the total lithium in solid solution in said modified highly purified quartz is increased to a final level of 0.60 to 1.00 ppm.
A method of modifying commercially available highly purified quartz powder having a low level of naturally occurring lithium for use in cladding a fiber optic cable, said method comprising:
- a) forming a solution of a lithium doping agent;
- b) blending said commercially available highly purified quartz powder with said doping solution to provide a blended mass with a given level of lithium comprising lithium of said doping solution coated onto said highly purified quartz powder and the low level of naturally occurring lithium of said highly purified quartz powder and said given level being in the range of 0.80 to 2.0 ppm;
- c) gassing said blended mass with a gas heated to a temperature of at least 1000° C. for a time to dope said commercially available highly purified powder with lithium in said doping solution;
- and,
- d) controlling the amount of lithium from said doping solution that is doped into said commercially available highly purified quartz powder so the total lithium in solid solution in said modified commercially available highly purified quartz powder is increased to final level 0.60-1.00 ppm.
Dependencies are inferred from the claim text.