Method for preparing PBAT laminated membrane composite material and uses
AssigneeShandong Benefit New Material Co., Ltd.
InventorPeng Xing
Life of this patent
Estimating the term…
Abstract
A method for preparing a PBAT laminated membrane composite material uses PBAT or a material with PBAT as the main component and other biodegradable plastic or superfine calcium carbonate in a mixture. The temperature of the mixture is increased by means of a lamination machine segment by segment, the material is heated slowly to a molten state, and the temperature of a rolling shaft is controlled by introducing cold water to the rolling shaft when the lamination machine conducts membrane lamination, so that the temperatures of rolling wheels and the laminated membrane are controlled.
Claims10
A method for preparing a PBAT film composite, comprising the following steps of:
- I. putting PBAT or a mixture of 100 weight parts of PBAT and 5-40 weight parts of a biodegradable plastic or 5-40 weight parts of super-fine calcium carbonate, as a base stock, into a mixing tank (1), mixing, heating and drying the base stock;
- II. conveying the base stock dried in step I to a storage bin (3) of a coating machine by a raw material conveyor (2);
- III. sending the base stock in the storage bin (3) from step II into the coating machine via a feed port (4), heating and pushing the base stock using a screw (5), wherein the coating machine is divided into a plurality of heating segments along a direction of the screw (5), and temperatures of the heating segments gradually rise to the melting point of the base stock along the direction of the screw (5), and sending the melted base stock to a coating tool (7) of the coating machine via a material conveying elbow (6);
- VI. pushing a coating machine table (15) to a selected position using advance guide wheels (16) at a bottom of the coating machine table (15) such that the coating tool (7) as described in step III is positioned between two rollers (10) of the coating machine table (15), turning the coating tool (7) by a fixed sliding base (12) which is driven by a transverse cylinder (11) such that the coating tool (7) is positioned on a central line between the two rollers (10) of the coating machine table (15), finally raising the coating machine table (15) under control of a pushing oil hydraulic cylinder (18) such that the coating central line between the two rollers (10) keeps a selected distance away from a discharge opening of the coating tool (7);
- V. conveying a substrate to a position between the two rollers (10) of the coating machine table (15) by a substrate shaft, controlling the coating machine to cover a base stock film on a substrate, controlling a complexing strength between the base stock and the substrate by controlling a pressure between the two rollers (10) through a transverse air cylinder (11), wherein the substrate is any one of paper, non-woven fabric or thin paperboard;
- pumping cooling water into the rollers to control a temperature of the rollers to be 20-30° C., thus ensuring that a melted film (9) is capable of being quickly cooled and solidified after being covered on the substrate, complexing the film (9) on the substrate and separating the film from the rollers (10).
Dependencies are inferred from the claim text.