Concrete compositions and method for making same
AssigneeNew Technology Solutions, LLC
InventorsDavid M. Brassard, Dwayne Dillingham
Life of this patent
Estimating the term…
Abstract
A process of preparing a concrete mixture includes the following steps: (a) providing a nano-sized non-sand silica and water; (b) mixing the non-sand silica with the water to form a silica-water mixture; (c) mixing an acid into the silica-water mixture to form a treated water; (d) mixing Portland cement and the treated water for a time sufficient to wet the Portland cement with the treated water to form a Portland/treated-water mixture; (e) mixing aggregate and the Portland-treated-water mixture to form an uncured concrete; and (f) allowing the uncured concrete to cure to form a cured concrete.
Claims25
A process of preparing a concrete mixture, including the following steps in order:
- (i) providing a nano-sized non-sand silica composition and water;
- (ii) mixing the non-sand silica with the water to form a silica-water mixture;
- (iii) mixing an acid into the silica-water mixture to form a treated water, wherein the treated water contains sufficient acid to obtain a treated water pH in the range from pH 2 to pH 4;
- (iv) combining Portland cement with the treated water and mixing;
- and
- (v) combining aggregate with the Portland cement-treated water mixture and mixing, wherein the combined Portland cement, aggregate and treated water form an uncured concrete composition,
- wherein the nano-sized non-sand silica composition is formed from one or more silicates, siloxanes, polyhedral oligomeric silsesguioxane (POSS), silsesguioxanes, silicone MQ resins, wet or dry silicas, fused or ground quartzes, colloidal silicas, precipitated silicas, organosilane-treated precipitated silicas, fumed silicas and organosilane-treated fumed silicas and has a particle in the range from about 1 nanometer (nm) to about 1000 nm,
- wherein the uncured concrete composition contains from about 0.001 weight percent to about 0.1 weight percent of the non-sand silica composition, based on the total weight of the uncured concrete composition,
- wherein the uncured concrete composition has an initial, post-mixing, temperature and where the uncured concrete composition produces a curing exotherm that results in a temperature increase of about 15° C. or less with respect to the initial temperature of the uncured concrete composition, and
- wherein a cured concrete composition produced from the concrete mixture exhibits a compressive strength of at least about 7000 psi after 28 days.
7 more elements
A concrete product prepared by the following steps in order:
- (I) providing a nano-sized non-sand silica composition and water;
- (II) mixing the non-sand silica with the water to form a silica-water mixture;
- (III) mixing an acid into the silica-water mixture to form a treated water, wherein the treated water contains sufficient acid to obtain a treated water pH in the range from pH 2 to pH 4;
- (IV) combining Portland cement with the treated water and mixing;
- and
- (V) combining aggregate with the Portland cement treated-water mixture and mixing, wherein the combined Portland cement, aggregate and treated water form an uncured concrete composition,
- wherein the nano-sized non-sand silica composition is formed from one or more silicates, siloxanes, polyhedral oligomeric silsesquioxane (POSS), silsesquioxanes, silicone MQ resins, wet or dry silicas, fused or ground quartzes, colloidal silicas, precipitated silicas, organosilane-treated precipitated silicas, fumed silicas and organosilane-treated fumed silicas and has a particle in the range from about 1 nanometer (nm) to about 1000 nm,
- wherein the uncured concrete composition contains from about 0.001 weight percent to about 0.1 weight percent of the non-sand silica composition, based on the total weight of the uncured concrete composition, and allowing the uncured concrete to cure to form a cured concrete,
- wherein the uncured or cured concrete composition made by the foregoing steps provides one or a combination of any two or more of features A, B, C and/or D:
- A. during Step (IV) the uncured concrete composition substantially does not bleed liquid water, in contrast to conventional concrete mixtures which do bleed water during the curing process;
- B. the uncured concrete composition has an initial, post-mixing, temperature and where the uncured concrete composition produces a curing exotherm that results in a temperature increase of about 15° C. or less with respect to the initial temperature of the uncured concrete composition;
- C. the cured concrete composition exhibits no cracking during cure, when applied over a proper base, even without saw cutting the concrete composition to prevent cracks from forming during cure as a result of thermal expansion during curing;
- and
- D. the cured concrete composition exhibits a compressive strength of at least about 7000 psi after 28 days.
11 more elements
An uncured concrete composition comprising:
- (a) water;
- (b) nano-sized non-sand silica composition and water;
- (c) at least one acid composition;
- (d) Portland cement;
- (e) sand;
- and
- (f) at least one aggregate,
- wherein the nano-sized non-sand silica composition is formed from one or more silicates, siloxanes, polyhedral oligomeric silsesquioxane (POSS), silsesquioxanes, silicone MQ resins, wet or dry silicas, fused or ground quartzes, colloidal silicas, precipitated silicas, organosilane-treated precipitated silicas, fumed silicas and organosilane-treated fumed silicas and has a particle in the range from about 1 nanometer (nm) to about 1000 nm,
- wherein the uncured concrete composition contains from about 0.001 weight percent to about 0.1 weight percent of the non-sand silica composition, based on the total weight of the uncured concrete composition,
- wherein the combination of components (a) through (f) yield a concrete composition that has a low exotherm during cure, where the uncured concrete composition has an initial, post-mixing, temperature and where the uncured concrete composition produces a curing exotherm that results in a temperature increase of about 15° C. or less with respect to the initial temperature of the uncured concrete composition, and
- wherein a cured concrete composition produced from the uncured concrete composition exhibits a compressive strength of at least about 7000 psi after 28 days.
8 more elements