# US 10,483,552 B2 · Catalyst comprising cobalt core and carbon shell for alkaline oxygen reduction and method for preparing the same

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 10,483,552 B2
- Document ID: US10483552B2
- Status: Granted
- Kind: B2
- Application number: 15/910,304
- Filed: 2018-03-02
- Published: 2018-09-06
- Granted: 2019-11-19
- Earliest claimed: 2017-03-06
- Assignees: Korea Institute of Science and Technology
- Applicants: Korea Institute of Science and Technology
- Inventors: Sung Jong Yoo; Jue-hyuk Jang; So Young Lee; Jin Young Kim; Jong Hyun Jang; Hyoung-Juhn Kim; Namgee Jung; Hyun Seo Park
- Web page: https://patentgrep.com/patent/US10483552B2

## CPC

- H01M 4/9041: {Metals or alloys (H01M4/92 takes precedence)}
- B01J 21/18: Carbon
- B01J 23/75: Cobalt
- H01M 4/88: Processes of manufacture
- H01M 4/9083: {on carbon or graphite}
- H01M 2008/1095: {Fuel cells with polymeric electrolytes}
- Y02E 60/50: Fuel cells
- H01M: PROCESSES OR MEANS, e.g. BATTERIES, FOR THE DIRECT CONVERSION OF CHEMICAL ENERGY INTO ELECTRICAL ENERGY
- B01J: CHEMICAL OR PHYSICAL PROCESSES, e.g. CATALYSIS OR COLLOID CHEMISTRY; THEIR RELEVANT APPARATUS
- Y02E: REDUCTION OF GREENHOUSE GAS [GHG] EMISSIONS, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION

## Abstract

A catalyst containing a carbon support and a core-shell nanoparticle supported on the carbon support, wherein a core of the core-shell nanoparticle is cobalt metal not containing a heterogeneous element and the shell contains carbon. The catalyst for an oxygen reduction reaction of the present disclosure is a catalyst in which the cobalt core-carbon shell nanoparticle is supported on the carbon support through ligand stabilization and heat treatment. The catalyst can be synthesized to have high dispersibility. In particular, it can be used as an electrode catalyst of a cathode to improve the oxygen reduction activity and durability of a fuel cell operating under an alkaline atmosphere.

## Claims

### Claim 1

A method for preparing a catalyst, consisting of:
(a) preparing a dispersion by dispersing a carbon support in a solvent;
(b) preparing a mixture solution by mixing the dispersion with a cobalt precursor and oleylamine;
(c) preparing a catalyst precursor by heat-treating the mixture solution at a low temperature of 250-350° C. under an inert gas atmosphere, wherein an oleylamine-coated cobalt oxide nanoparticle is supported on the carbon support in the catalyst precursor; and
(d) preparing a catalyst by heat-treating the catalyst precursor at a high temperature of 550-800° C. under the inert gas atmosphere, wherein the catalyst contains the carbon support and a core-shell nanoparticle supported on the carbon support,
wherein the core of the core-shell nanoparticle is cobalt metal without having the heterogeneous element and the shell of the core-shell contains carbon.

### Claim 2 (depends on 1)

The method for preparing a catalyst according to claim 1, wherein the carbon support is one or more selected from carbon black, graphite and carbon nanotube.

### Claim 3 (depends on 1)

The method for preparing a catalyst according to claim 1, wherein the solvent is one or more selected from 1-octadecene, water, methanol, ethanol, propanol, butanol, toluene and ethylene glycol.

### Claim 4 (depends on 1)

The method for preparing a catalyst according to claim 1, wherein the cobalt precursor is one or more selected from cobalt acetylacetonate, cobalt acetylacetate, cobalt acetate, cobalt halide, cobalt nitrate, cobalt hydroxide and cobalt carbonyl complex.

### Claim 5 (depends on 1)

The method for preparing a catalyst according to claim 1, wherein the heat treatment at a low temperature in (c) is performed for 30 minutes to 3 hours.

### Claim 6 (depends on 1)

The method for preparing a catalyst according to claim 1, wherein the heat treatment at a high temperature in (d) is performed for 30 minutes to 2 hours.