US 10,472,429 B2 · Package of water absorbent resin powder

Abstract

A method according to the present invention for producing water absorbent resin powder is a method for producing water absorbent resin having a surface cross-linked structure, and includes: a polymerization step in which an unsaturated monomer aqueous solution is polymerized; a drying step in which a hydrogel cross-linked polymer obtained in the polymerization step is dried; a surface treatment step in which the hydrogel cross-linked polymer or a dried hydrogel cross-linked polymer is subjected to a surface treatment; and a sorting step, carried out after the drying step, in which a foreign matter included in a water absorbent resin is color-sorted from the water absorbent resin entirely or partially. As a result, it is possible to obtain a water absorbent resin which has high properties and is less likely to be colored. In this way, there is provided the water absorbent resin powder production method in which the color sorting technique is used to remove foreign matters from the water absorbent resin.

Claims1

Dependent claims

A package of water absorbent resin powder obtained by carrying out cross-linking polymerization with respect to an unsaturated monomer containing acrylic acid and/or salt thereof as a main component,

said package comprising a non-permeable bag or a non-permeable container containing 20 kg to 200000 kg of the water absorbent resin powder as each package, a production volume of the package being 100 Mton or more,
said water absorbent resin powder satisfying the following properties:
(a) an amount of a foreign matter included in the water absorbent resin powder and being a nonmagnetic and black or brown organic substance is 5 mm2/100 g or less;
(b) an absorbency against pressure (AAP:
0.90 g) is 20 g/g or more and 60 g/g or less;
(c) an amount of fine powder whose particle diameter is 150 μm or less is 0 mass % or more and 5 mass % or less, and a mass average particle diameter (D50) is 200 μm or more and 550 μm or less, and a particle size distribution logarithmic standard deviation (σζ) is 0.20 or more and 0.40 or less, defined by standard sieve classification.

3 more elements

Dependencies are inferred from the claim text.

Package of water absorbent resin powder

Life of this patent

Package of water absorbent resin powder

Life of this patent

Abstract

Claims1