Colored biaxially stretched polyester film for metal plate attachment and forming processing
AssigneeTeijin Film Solutions Limited
InventorsNaoki Iyo, Mitsuo Tojo
Life of this patent
Estimating the term…
Abstract
A colored biaxially stretched polyester film for metal plate attachment and forming processing, includes three layers: opposite surface layers (layers A) that contain substantially no coloring pigment and are made of a copolyester having an intrinsic viscosity of 0.65 to 0.80 and a melting point (TmA) of 230 to 260° C.; and a core layer (layer B) that has a coloring pigment content of more than 10 wt % and 50 wt % or less and is made of a copolyester having an intrinsic viscosity of 0.55 to 0.70 and a melting point (TmB) of 230 to 260° C. The film has a surface roughness within a range of 10 to 40 nm, and (TmB−TmA) is 4° C. or less.
Claims14
A colored biaxially stretched polyester film for metal plate attachment and forming processing, comprising three layers:
- opposite surface layers (layers A), each of which consisting of (i) a copolyester having an intrinsic viscosity of 0.65 to 0.80 and a melting point of 230 to 260° C., (ii) perfectly spherical inert particles having an average particle size of 1.5 to 5.0 μm, wherein the perfectly spherical inert particles are silica, and (iii) substantially no coloring pigment;
- and
- a core layer (layer B) that is made of a copolyester composition, said copolyester composition having an intrinsic viscosity of 0.55 to 0.70 and a melting point of 230 to 260° C., and has a coloring pigment content of more than 10 wt % and 50 wt % or less,
- wherein the film has a surface roughness within a range of 10 to 40 nm, and the melting points of the copolyester of the layers A and the copolyester composition of the layer B satisfy the following equation (1):
- TmB−TmA≤4° C. (1)
- wherein TmA represents the melting point of the copolyester of the layers A, and TmB represents the melting point of the copolyester composition of the layer B, and
- wherein TmB≥TmA.
A colored biaxially stretched polyester film for metal plate attachment and forming processing, comprising three layers:
- opposite surface layers (layers A), each of which consisting of:
- (i) a first copolyester composition consisting of a blend of a copolyester and a homopolyester, the first copolyester composition having an intrinsic viscosity of 0.65 to 0.80 and a melting point of 230 to 260° C.,
- (ii) perfectly spherical inert particles having an average particle size of 1.5 to 5.0 μm, wherein the perfectly spherical inert particles are silica, and
- (iii) substantially no coloring pigment;
- and
- a core layer (layer B) that is made of a second copolyester composition, said second copolyester composition having an intrinsic viscosity of 0.55 to 0.70 and a melting point of 230 to 260° C., and has a coloring pigment content of more than 10 wt % and 50 wt % or less,
- wherein the film has a surface roughness within a range of 10 to 40 nm, and the melting points of the first and second copolyester compositions satisfy the following equation (1):
- TmB−TmA≤4° C. (1)
- wherein TmA represents the melting point of the first copolyester composition of the layers A, and TmB represents the melting point of the second copolyester composition of the layer B, and
- wherein TmB≥TmA.
Dependencies are inferred from the claim text.