US 10,351,479 B2Granted
Maintenance-free stone tile, coating agent therefor, and method for producing the tile
AssigneeKyushu Hightec Corporation
InventorMasaki Watanabe
Life of this patent
Estimating the term…
Abstract
A maintenance-free stone tile is provided in which a super hard coating film having a pencil hardness corresponding to 12H or more (preferably to 12 to 15H) is used to produce a finish having a deep material feeling and a high quality, and glossiness of 80 or more, and be further able of keeping the coating layer good in water resistance, antifouling property, slipperiness, adhesiveness and no crack, over a long term, on a surface of a stone tile, such as a marble, artificial stone, terrazzo or ceramic tile. The tile is a stone tile having an inorganic coating layer causing a surface of the stone to have a pencil hardness of 12H or more and a mirror surface glossiness of 80 or more.
Claims3
A maintenance-free stone tile, comprising:
- a stone tile selected from the group consisting of marble and terrazzo;
- and
- an inorganic glassy protective coating layer formed on a surface of the stone tile,
- wherein the inorganic glassy protective coating layer has an outer surface having a pencil hardness of a value corresponding to 12H or more in the case of measuring the outer surface on the basis of correlative data between a pencil hardness test and an abrasion resistance test;
- a thickness of the coating of 20 to 50 μm;
- a surface roughness Rmax of 0.8 s (μm) or less;
- a mirror surface glossiness of 80 or more;
- dry slip properties of 0.6 or more;
- a wet slipperiness of 0.5 or more;
- and a surface resistance value of 1011Ω or less,
- wherein the inorganic glassy protective coating layer is formed of an inorganic glassy coating agent, and
- wherein the inorganic glassy coating agent comprises a main ingredient which comprises:
- an alkoxysilane essentially consisting of a mixture of a tetrafunctional alkoxysilane and a trifunctional alkoxysilane at a ratio of tetrafunctional silane 10%/trifunctional silane 90% to tetrafunctional silane 20%/trifunctional silane 80%,
- a silane coupling agent that has an epoxy functional group;
- and colloidal silica superfine particles having an average particle size of 5 to 20 nm;
- wherein provided that the proportion of the main ingredient being regarded as 100% by weight,
- the alkoxysilane is from 30 to 50% by weight;
- the silane coupling agent is from 5 to 20% by weight;
- the colloidal silica superfine particles are from 20 to 40% by weight;
- and
- phosphoric acid is in the range from 0.1 to 5.0% by weight or
- a titanium based catalyst and/or an aluminum based catalyst is in the range from 0.1 to 20.0% by weight,
- added as a catalyst for heightening reaction hardenability,
- wherein the inorganic glassy coating agent has a viscosity of 3.6 cSt to 6 cSt (mm2/s), and
- wherein the inorganic glassy coating agent provides an outer surface having a pencil hardness of a value corresponding to 12H or more in the case of measuring the outer surface on the basis of correlative data between a pencil hardness test and an abrasion resistance test.
22 more elements
An inorganic glassy coating agent for a maintenance-free stone tile, comprising a main ingredient which comprises:
- an alkoxysilane essentially consisting of a mixture of a tetrafunctional alkoxysilane and a trifunctional alkoxysilane at a ratio of tetrafunctional silane 10%/trifunctional silane 90% to tetrafunctional silane 20%/trifunctional silane 80%,
- a silane coupling agent that has an epoxy functional group;
- and colloidal silica superfine particles having an average particle size of 5 to 20 nm;
- wherein provided that the proportion of the main ingredient being regarded as 100% by weight,
- the alkoxysilane is from 30 to 50% by weight;
- the silane coupling agent is from 5 to 20% by weight;
- the colloidal silica superfine particles are from 20 to 40% by weight;
- and
- phosphoric acid is in the range from 0.1 to 5.0% by weight or
- a titanium based catalyst and/or an aluminum based catalyst is in the range from 0.1 to 20.0% by weight,
- added as a catalyst for heightening reaction hardenability,
- wherein the inorganic glassy coating agent has a viscosity of 3.6 cSt to 6 cSt (mm2/s),
- wherein the inorganic glassy coating agent provides an outer surface having a pencil hardness of a value corresponding to 12H or more in the case of measuring the outer surface on the basis of correlative data between a pencil hardness test and an abrasion resistance test, and
- wherein the inorganic glassy coating agent for a maintenance-free stone tile is to be applied to a stone tile selected from the group consisting of marble and terrazzo.
11 more elements
A method for producing a maintenance-free stone tile, comprising:
- a step of adjusting a viscosity of the inorganic glassy coating agent of claim 2 to 3.6 cSt to 6 cSt (mm2/s), and then coating a floor surface of a stone that is obtained by roughening a surface of the stone beforehand by diamond grinding, the stone being selected from the group consisting of marble and terrazzo,
- a step of hardening the coating agent at ambient temperature in one hour to one day after the coating treatment to have a pencil hardness corresponding to 12H or more when the pencil hardness is measured on the basis of correlative data between a pencil hardness test and an abrasion resistance test;
- and
- a subsequent step of grinding the outer surface of the resultant coating layer with a diamond grindstone, whereby the resultant outer surface has a surface roughness Rmax of 0.8 s or less and a mirror surface glossiness of 80 or more.
1 more element
Dependencies are inferred from the claim text.