Solder alloy and joint thereof
AssigneeNihon Superior Co., Ltd.
InventorsTetsuro Nishimura, Shoichi Suenaga, Takashi Nozu, Motonori Miyaoka, Yasufumi Shibata
Life of this patent
Estimating the term…
Abstract
A silver electrode joint having a high joint strength obtained by actively minimizing the particle size of a silver-zinc intermetallic compound at the solidification point. A joint obtained by joining an article to be joined, the joint including silver at least as the surface layer thereof, using a solder alloy which comprises 2-9 wt % of zinc, 0.0001-0.1 wt % of manganese and the balance consisting of tin, the solder joint having a joint interface wherein the particle size of a silver-zinc intermetallic compound, which is formed by silver being the surface layer of the article to be joined and zinc in the solder alloy, is 5 μm or less.
Claims3
A solder joint, comprising:
- a joint in which at least a surface layer is silver and is joined by a solder alloy composed of 2 to 9 weight % of zinc, 0.0001 to 0.1 weight % of manganese, and a remainder of tin, the solder joint having a joint boundary in which a silver-zinc intermetallic compound formed of silver of the surface layer of the joint and zinc in the solder alloy has a grain size of 5 μm or less;
- wherein a solder plating with the solder alloy is applied in advance to a first joint surface and a second joint surface of the joint, and the first solder plating and the second solder plating are heated to be molten while the first solder plating and the second solder plating are brought into contact with each other, and then solidified;
- and wherein a heating/melting temperature of the solder alloy is 230° C.-300° C.
A solder joining method, comprising:
- plating a first joint surface and a second joint surface of a joint to have a solder plating in which at least a surface layer is silver and is plated in advance with a solder alloy composed of 2 to 9 weight % of zinc, 0.0001 to 0.1 weight % of manganese, and a remainder of tin;
- heating to a temperature of 230° C.-300° C. the solder platings on the first joint surface and the second joint surface to be molten while bringing the solder platings into contact with each other;
- and
- cooling the solder platings until the solder platings are solidified.