Sheet for thermal bonding and sheet for thermal bonding with affixed dicing tape

A sheet for thermal bonding comprising fine metal particles in an amount in a range of 70 to 98% by weight,

• the sheet for thermal bonding having a carbon concentration of 15% by weight or less obtained by energy dispersive X-ray spectrometry after being heated from 23° C. to 400° C. in the air at a heating rate of 10° C./min,
• the sheet for thermal bonding having a tensile modulus of 10 to 3,000 MPa obtained by the following tensile test method:
• the tensile test method comprising the steps of:
• (1) preparing a sheet for thermal bonding having a thickness of 200 μm, a width of 10 mm, and a length of 40 mm as a test sample;
• (2) performing a tensile test under conditions of a distance between chucks of 10 mm, a tensile speed of 50 mm/min, and a temperature of 23° C. to obtain a stress-strain diagrammatic view;
• and
• (3) defining a slope of a straight line portion of the stress-strain diagrammatic view as the tensile modulus, wherein
• the sheet for thermal bonding includes at least one thermally-decomposable binder selected from the group consisting of an acrylic resin and a polycarbonate resin,
• the fine metal particles, which are an aggregate of fine metal particles, are made of at least one selected from the group consisting of silver, copper, silver oxide, and copper oxide, and
• a peak when differential thermal analysis is performed while heating from 23° C. to 500° C. in the air at a heating rate of 10° C./min is present at 150° C. to 350° C.