US 10,293,408 B2Granted

Method and device for producing shots

AssigneeSintokogio, Ltd.

InventorsMasayuki Ishikawa, Naoya Tanuma, Tomohiro Togari

Life of this patent

Estimating the term…

Loading patent…

Abstract

A method and device for producing shots are provided where the yield is improved. In a space (5) for forming molten drops, which space is surrounded by water (1) in a tank (20), by a cover (3) to cover an area surrounding a disc (2) that is located above the water and rotates, and by a tundish (4) that penetrates through the cover, a gas is discharged though an opening (6) that is formed in the cover and the film (9) of the water is formed on the inner surface of the cover. The molten metal (10) flows through the hole (11) in the bottom of the tundish to be supplied onto the rotating disc. The molten drops are formed by centrifugal force from the molten metal that has been supplied to the disc. Then the molten drops are caused to collide with the film of the water on the inner surface of the cover, to be divided into the droplets that are smaller than the molten drops. The droplets are cooled and solidified.

Claims14

Dependent claims

A method for producing shots in a space for forming molten drops, wherein the space is covered by a cover and by a tundish, the cover being provided to cover water in a tank and to cover an area surrounding a disc that is located above the water and rotates, and the tundish penetrating through the cover, the method comprising the steps of:

exhausting gas through an opening, which gas is generated in the space for forming the molten drops;
forming a film of water on an inner surface of the cover;
supplying molten metal to inject molten metal into the tundish to supply the molten metal onto the rotating disc by causing the molten metal to flow through a hole in a bottom of the tundish;
forming molten drops from the molten metal by centrifugal force, which molten metal is supplied onto the rotating disc;
dividing the molten drops into droplets that are smaller than the molten drops by causing the molten drops to collide with the inner surface of the cover, on which the film of the water is formed in the step of forming the film of water, and then to cool and solidify the droplets,
wherein in the step of exhausting gas a valve that is connected to the opening is controlled to be open if pressure in the space for forming the moltent drops exceeds an upper limit or closed if the pressure in the space for forming the molten drops falls below a lower limit.

3 more elements

exhausting gas through an opening, which gas is generated in the space for forming the molten drops;
forming a film of water on an inner surface of the cover;
supplying molten metal to inject molten metal into the tundish to supply the molten metal onto the rotating disc by causing the molten metal to flow through a hole in a bottom of the tundish;
forming molten drops from the molten metal by centrifugal force, which molten metal is supplied onto the rotating disc;
dividing the molten drops into droplets that are smaller than the molten drops by causing the molten drops to collide with the inner surface of the cover, on which the film of the water is formed in the step of forming the film of water, and then to cool and solidify the droplets,
wherein in the step of exhausting the gas a kind and a concentration of the gas in the space for forming the molten drops are detected, so that a valve, which is connected to the opening, is controlled to be open or closed to stabilize the concentration of the gas in the space for forming the molten drops.

3 more elements

Dependencies are inferred from the claim text.