Resistance spot welding method
AssigneeNippon Steel & Sumitomo Metal Corporation
InventorsHiroki Fujimoto, Hatsuhiko Oikawa, Shintaro Yamanaka
Life of this patent
Estimating the term…
Abstract
A resistance spot welding method including: a pulsation process of clamping a sheet assembly of two or more overlapped steel sheets including at least one high tensile steel sheet using a pair of welding electrodes that are connected to a spot welding power source employing an inverter direct current method, and performing plural repetitions of current passing and current pass stopping, while pressing the steel sheets with the welding electrodes; and a continuous current pass process in which, after the pulsation process, current is passed continuously for a longer period of time than a maximum current pass time of the pulsation process, while pressing the steel sheets with the welding electrodes.
Claims11
A resistance spot welding method comprising:
- providing a sheet assembly of two or more overlapping steel sheets including at least one high-tensile steel sheet, wherein each pair of the two or more overlapping steel sheets includes an interface in the area of overlap;
- clamping the sheet assembly using a pair of welding electrodes that are connected to a spot welding power source employing an inverter direct current method;
- performing a pulsation process comprising passing a pulse wave of current through said steel sheets, stopping current passage through said steel sheets, and repeating the passing of a pulse wave of current through said steel sheets and the stopping of current passage through said steel sheets, while pressing the steel sheets with the welding electrodes, thereby forming a nugget at the interface between the steel sheets, wherein a current value of the current passes in the pulsation process is from 7.0 kA to 14.0 kA and current passing times in the current passes in the pulsation process are each from 10 milliseconds to 60 milliseconds;
- and, after the pulsation process,
- passing current continuously for a longer period of time than a current passing time of each repetition, while pressing the steel sheets with the welding electrodes and thereby growing the nugget.
A resistance spot welding method comprising:
- providing a sheet assembly of two or more overlapping steel sheets including at least one high-tensile steel sheet, wherein each pair of the two or more overlapping steel sheets includes an interface in the area of overlap;
- clamping the sheet assembly using a pair of welding electrodes that are connected to a spot welding power source employing an inverter direct current method;
- performing a pulsation process comprising passing a pulse wave of current through said steel sheets, stopping current passage through said steel sheets, and repeating the passing of a pulse wave of current through said steel sheets and the stopping of current passage through said steel sheets, while pressing the steel sheets with the welding electrodes, thereby forming a nugget at the interface between the steel sheets, wherein current passing times in the current passes in the pulsation process are each from 10 milliseconds to 60 milliseconds;
- and, after the pulsation process,
- passing current continuously for a longer period of time than a current passing time of each repetition, while pressing the steel sheets with the welding electrodes and thereby growing the nugget, wherein a current value of a current pass in the continuous current passing process is from 5.0 kA to 12.0 kA and a current pass time in the continuous current passing process is from 100 milliseconds to 500 milliseconds.
Dependencies are inferred from the claim text.