Resin mixture, reaction resin—mortar, multi-component mortar system, and their application

A reaction resin mortar, comprising:

• a resin mixture comprising:
• at least one compound that can be radically polymerized,
• at least one first polymerization inhibitor, which is selected from the group consisting of stable N-oxyl-radicals and 4-hydroxy-3,5-di-tert-butyl toluene, and
• at least one first reactive diluent, which is selected from the group consisting of 1,3-dicarbonyl compounds with the formula (I)
• in which
• R1 represents a straight-chained or branched, optionally substituted C1-C6-alkyl group;
• R3 represents hydrogen or a straight-chained or branched, optionally substituted C1-C6-alkyl group, a C1-C6-alkoxy group, or a methacryloyloxy group with the formula (II)
• in which X represents a methylene glycol, ethylene glycol, or propylene glycol group, and n an integer with a value from 1 up to including 6,
• R2 represents hydrogen, a straight-chained or branched, optionally substituted C1-C6-alkyl group or a C1-C6-alkoxy group, or together with R3 forms an optionally substituted five or six-membered aliphatic ring, which optionally comprises heteroatoms in or at the ring;
• or 1,3-dicarbonyl compounds with the general formula (III)
• in which
• R4 represents a bivalent or polyvalent alcohol,
• X represents an integer between 1 and 6, and
• R1 and R2 are the same as defined above,
• wherein the ratio of at least one 1,3-dicarbonyl compound and the polymerization inhibitor ranges from 30:1 to 150:1,
• wherein the reactive diluent is included in an amount of from 1 to 15% by weight of the resin mixture and the at least one first polymerization inhibitor is included in an amount of from 0.005 to 2% by weight of the resin mixture, and
• wherein an Mn metal salt is excluded from the resin mixture, and
• wherein the viscosity of the resin mixture ranges from 200 to 800 mPa·s, and
• an inorganic and/or organic aggregate.

A reaction resin mortar, comprising:

• a resin mixture comprising:
• at least one compound that can be radically polymerized,
• at least one first polymerization inhibitor, which is selected from the group consisting of stable N-oxyl-radicals and 4-hydroxy-3,5-di-tert-butyl toluene, and
• at least one first reactive diluent, which is selected from the group consisting of 1,3-dicarbonyl compounds with the formula (1)
• in which
• R1 represents a straight-chained or branched, optionally substituted C1-C6-alkyl group;
• R3 represents hydrogen or a straight-chained or branched, optionally substituted C1-C6-alkyl group, a C1-C6-alkoxy group, or a methacryloyloxy group with the formula (II)
• in which X represents a methylene glycol, ethylene glycol, or propylene glycol group, and n an integer with a value from 1 up to including 6,
• R2 represents hydrogen, a straight-chained or branched, optionally substituted C1-C6-alkyl group or a C1-C6-alkoxy group, or together with R3 forms an optionally substituted five or six-membered aliphatic ring, which optionally comprises heteroatoms in or at the ring;
• or 1,3-dicarbonyl compounds with the general formula (III)
• in which
• R4 represents a bivalent or polyvalent alcohol,
• X represents an integer between 1 and 6, and
• R1 and R2 are the same as defined above,
• wherein the ratio of at least one 1,3-dicarbonyl compound and the polymerization inhibitor ranges from 30:1 to 150:1,
• wherein the reactive diluent is included in an amount of from 1 to 15% by weight of the resin mixture and the at least one first polymerization inhibitor is included in an amount of from 0.005 to 2% by weight of the resin mixture, and
• wherein an Mn accelerant is excluded from the resin mixture, and
• wherein the viscosity of the resin mixture ranges from 200 to 800 mPa·s, and
• an inorganic and/or organic aggregate.