Method for producing a master mixture based on carbonaceous nanofillers and super plasticiser, and the use thereof in hardenable inorganic systems

A method of improving the resistance to freezing and to the diffusion of liquid of a curable inorganic system, the method comprising adding a master batch, for improving the resistance to freezing and to the diffusion of liquid of a curable inorganic system, and water separately and directly into a kneading appliance comprising at least one curable inorganic system, in order to ensure a content of the fillers ranging from 0.0001% to 0.02% by weight, with respect to the curable inorganic system, and a water/curable inorganic system ratio by weight ranging from 0.2 to 1.5

• wherein the master batch comprises at least one superplasticizer and fillers, the fillers comprising at least one component selected from the group consisting of carbon nanotubes, carbon nanofibres, and graphene, at a content by weight of between 0.1% and 25%, with respect to the total weight of the master batch, capable of being obtained according to a process for the preparation of a master batch, comprising:
• (i) introduction into a kneader and then kneading of the fillers and of at least one superplasticizer, optionally in the presence of a water-soluble dispersing agent, in order to form a homogeneous mixture in the solid form or in the pasty composition form;
• (ii) extrusion of said mixture in the solid form in order to obtain a master batch in the solid form;
• (iii) optionally, dispersion of said master batch in the solid form in a superplasticizer identical to or different from that of stage (i), or in a water-soluble dispersant, in order to obtain a master batch in the form of a pasty composition;
• and
• (iv) optionally, introduction of the master batch in the form of a pasty composition obtained in stage (iii), into a superplasticizer which is identical to or different from that of stage (iii), in order to obtain a master batch having a content of the fillers from 0.1 to 2% by weight.

A method of improving the adhesion between a curable inorganic system and metal or nonmetal reinforcements or reinforcers in the form of mineral fibers or reinforcers based on polymers in structural construction products, the method comprising adding a master batch, for improving the adhesion between a curable inorganic system and metal or nonmetal reinforcements or reinforcers in the form of mineral fibers or reinforcers based on polymers in structural construction products, and water separately and directly into a kneading appliance comprising at least one curable inorganic system, in order to ensure a content of the fillers ranging from 0.0001% to 0.02% by weight, with respect to the curable inorganic system, and a water/curable inorganic system ratio by weight ranging from 0.2 to 1.5

• wherein the master batch comprises at least one superplasticizer and fillers, the fillers comprising at least one component selected from the group consisting of carbon nanotubes, carbon nanofibres, and graphene, at a content by weight of between 0.1% and 25%, with respect to the total weight of the master batch, capable of being obtained according to a process for the preparation of a master batch, comprising:
• (i) introduction directly of the masterbatch into a kneader and then kneading of the fillers and of at least one superplasticizer, optionally in the presence of a water-soluble dispersing agent, in order to form a homogeneous mixture in the solid form or in the pasty composition form;
• (ii) extrusion of said mixture in the solid form in order to obtain a master batch in the solid form;
• (iii) optionally, dispersion of said master batch in the solid form in a superplasticizer identical to or different from that of stage (i), or in a water-soluble dispersant, in order to obtain a master batch in the form of a pasty composition;
• and
• (iv) optionally, introduction of the master batch in the form of a pasty composition obtained in stage (iii), into a superplasticizer which is identical to or different from that of stage (iii), in order to obtain a master batch having a content of the fillers from 0.1 to 2% by weight.

A method of reducing the phenomena of microcracking due to the various stresses in structural construction products, the method comprising adding a master batch, for reducing the phenomena of microcracking due to the various stresses in structural construction products, and water separately and directly into a kneading appliance comprising at least one curable inorganic system, in order to ensure a content of the fillers ranging from 0.0001% to 0.02% by weight, with respect to the curable inorganic system, and a water/curable inorganic system ratio by weight ranging from 0.2 to 1.5

• wherein the master batch comprises at least one superplasticizer and fillers, the fillers comprising at least one component selected from the group consisting of carbon nanotubes, carbon nanofibres, and graphene, at a content by weight of between 0.1% and 25%, with respect to the total weight of the master batch, capable of being obtained according to a process for the preparation of a master batch, comprising:
• (i) introduction into a kneader and then kneading of the fillers and of at least one superplasticizer, optionally in the presence of a water-soluble dispersing agent, in order to form a homogeneous mixture in the solid form or in the pasty composition form;
• (ii) extrusion of said mixture in the solid form in order to obtain a master batch in the solid form;
• (iii) optionally, dispersion of said master batch in the solid form in a superplasticizer identical to or different from that of stage (i), or in a water-soluble dispersant, in order to obtain a master batch in the form of a pasty composition;
• and
• (iv) optionally, introduction of the master batch in the form of a pasty composition obtained in stage (iii), into a superplasticizer which is identical to or different from that of stage (iii), in order to obtain a master batch having a content of the fillers from 0.1 to 2% by weight.