Loading patent…
AssigneeNano and Advanced Materials Institute Limited
InventorsYan Gao, Honggang Zhu, Yifei Yan, Bo Li, Man Lung Sham, Tung-Chai Ling
Estimating the term…
Synthetic aggregates are fabricated from greater than approximately 70 wt % waste starting materials. Starting materials may be selected from granulated ground blast furnace slag, waste concrete fines, or sewage sludge ash, and mixtures thereof. The starting materials are bound together by a hydraulic cementitious binder either added to the starting materials or formed in situ. The waste starting materials, binder, and water are formed into pellets and subjected to a hydraulic reaction and carbonation in an atmosphere of greater than approximately 50% carbon dioxide at temperatures less than approximately 100° C. The resulting synthetic aggregate has a crush strength after a period of hardening equal to or greater than approximately 0.5 MPa.
A synthetic aggregate fabricated from greater than approximately 70 wt % waste starting materials selected from granulated ground blast furnace slag, recycled concrete waste fines, or sewage sludge ash, and mixtures thereof, the starting materials being bound together by a hydraulic cementitious binder, the waste starting materials and binder having been formed into pellets and subjected to a hydraulic reaction and carbonation in an atmosphere of greater than approximately 50% carbon dioxide at temperatures less than approximately 100° C., the aggregate having a crush strength after a period of hardening equal to or greater than approximately 0.5 MPa wherein the carbonation occurs while the pellets are being formed and the density is less than about 1200 kg/m3.
A synthetic aggregate fabricated from greater than approximately 70 wt % waste starting materials selected from granulated ground blast furnace slag, recycled concrete waste fines, or sewage sludge ash, and mixtures thereof, the starting materials being bound together by a hydraulic cementitious binder, the waste starting materials and binder having been formed into pellets and subjected to a hydraulic reaction and carbonation in an atmosphere of greater than approximately 50% carbon dioxide at temperatures less than approximately 100° C., the aggregate having a crush strength after a period of hardening equal to or greater than approximately 0.5 MPa wherein the carbonation occurs after the pellets are formed and the density is above about 1700 kg/m3.
A synthetic aggregate fabricated from greater than approximately 70 wt % waste starting materials selected from granulated ground blast furnace slag, recycled concrete waste fines, or sewage sludge ash, and mixtures thereof, the starting materials being bound together by a hydraulic cementitious binder, the waste starting materials and binder having been formed into pellets and subjected to a hydraulic reaction and carbonation in an atmosphere of greater than approximately 50% carbon dioxide at temperatures less than approximately 100° C., the aggregate having a crush strength after a period of hardening equal to or greater than approximately 0.5 MPa wherein the aggregate is fabricated from the waste starting materials, binder, water and hydrogen peroxide and the density is less than 1200 kg/m3.
A synthetic aggregate fabricated from greater than approximately 70 wt % waste starting materials selected from sewage sludge ash, the starting materials being bound together by a hydraulic cementitious binder, the waste starting materials and binder having been formed into pellets and subjected to a hydraulic reaction and carbonation in an atmosphere of greater than approximately 50% carbon dioxide at temperatures less than approximately 100° C., the aggregate having a crush strength after a period of hardening equal to or greater than approximately 0.5 MPa and wherein the water absorption is less than approximately 20% and the pellets are treated with a silane-based agent.
Dependencies are inferred from the claim text.