Manufacturing process for striae-free multicomponent chalcogenide glasses via multiple fining steps
AssigneeThe United States of America as represented by the Secretary of the Navy
InventorsVinh Q. Nguyen, Mikhail Kotov, Daniel J. Gibson, Shyam S. Bayya, Jasbinder S. Sanghera, Gryphon A. Drake
Life of this patent
Estimating the term…
Abstract
The present invention provides a method for synthesizing high optical quality multicomponent chalcogenide glasses without refractive index perturbations due to striae, phase separation or crystal formation using a two-zone furnace and multiple fining steps. The top and bottom zones are initially heated to the same temperature, and then a temperature gradient is created between the top zone and the bottom zone. The fining and cooling phase is divided into multiple steps with multiple temperature holds.
Claims9
A method to make striae-free chalcogenide glass, comprising:
- loading chalcogenide glass precursors into an ampoule, sealing the ampoule, and placing the ampoule in a rocking furnace, wherein the rocking furnace comprises a top zone and a bottom zone, wherein the top and bottom zones are two independently controllable temperature zones;
- heating both the top and bottom zones at a rate of 3° C. per minute to a Step 1 temperature, wherein the Step 1 temperature is the same for both the top and bottom zones;
- maintaining the Step 1 temperature in the top and bottom zones while rocking the furnace at an inclination angle of ±45° for about 15 hours;
- increasing the temperature of the top zone at a rate of 3° C. per minute to a Step 3 top zone temperature and decreasing the temperature of the bottom zone at a rate of 3° C. per minute to a Step 3 bottom zone temperature while rocking the furnace at an inclination angle of ±45°, wherein there is a temperature gradient of 100° C. between the Step 3 top zone temperature and the Step 3 bottom zone temperature;
- setting the furnace to a vertical position and maintaining the Step 3 top zone temperature and the Step 3 bottom zone temperature for about 3 hours;
- decreasing the temperature of the top zone at a rate of 10° C. per minute to a Step 5 top zone temperature, decreasing the temperature of the bottom zone at a rate of 10° C. per minute to a Step 5 bottom zone temperature, and maintaining the Step 5 top zone temperature and Step 5 bottom zone temperature for about 3 hours, wherein the Step 5 top zone temperature is about 100° C. lower than the Step 3 top zone temperature, and wherein the Step 5 bottom zone temperature is about 100° C. lower than the Step 3 bottom zone temperature;
- decreasing the temperature of the top zone at a rate of 10° C. per minute to a Step 6 top zone temperature, decreasing the temperature of the bottom zone at a rate of 10° C. per minute to a Step 6 bottom zone temperature, and maintaining the Step 6 top zone temperature and Step 6 bottom zone temperature for about 3 hours, wherein the Step 6 top zone temperature is about 100° C. lower than the Step 5 top zone temperature, and wherein the Step 6 bottom zone temperature is about 100° C. lower than the Step 5 bottom zone temperature;
- decreasing the temperature of the top zone at a rate of 10° C. per minute to a Step 7 top zone temperature, decreasing the temperature of the bottom zone at a rate of 10° C. per minute to a Step 7 bottom zone temperature, and maintaining the Step 7 top zone temperature and Step 7 bottom zone temperature for about 30 minutes, wherein the Step 7 top zone temperature is at least 100° C. lower than the Step 6 top zone temperature, and wherein the Step 7 bottom zone temperature is at least 100° C. lower than the Step 6 bottom zone temperature;
- and
- removing the ampoule from the furnace and water quenching the glass.
Dependencies are inferred from the claim text.