# US 10,118,219 B2 · Semisolid casting/forging apparatus and method as well as a cast and forged product

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 10,118,219 B2
- Document ID: US10118219B2
- Status: Granted
- Kind: B2
- Application number: 15/022,119
- Filed: 2014-10-09
- Published: 2016-08-11
- Granted: 2018-11-06
- Earliest claimed: 2013-10-09
- Assignees: Tohoku University
- Applicants: Tohoku University
- Inventors: Masayuki Itamura; Kouichi Anzai
- Web page: https://patentgrep.com/patent/US10118219B2

## CPC

- B22D 18/02: Pressure casting making use of mechanical pressure devices, e.g. cast-forging (B22D18/04 takes precedence)
- B22D 17/007: {Semi-solid pressure die casting}
- B22D 17/229: {with exchangeable die part (B22D17/2245 takes precedence)}
- B22D 19/00: Casting in, on, or around objects which form part of the product (B22D23/04 takes precedence; alumino-thermic welding B23K23/00; coating by casting molten material on the substrate C23C6/00)
- B22D 19/04: for joining parts
- B22D 27/04: Influencing the temperature of the metal, e.g. by heating or cooling the mould
- B22D 27/11: making use of mechanical pressing devices
- B22D: CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES (shaping of plastics or substances in a plastic state B29C; metallurgical processing, selection of substances to be added to metal C21, C22)

## Abstract

An excellent cast and forged product that is superior in mechanical properties and has a microstructure and which may not only be a thin but also be a thick product can be made without using complicated process steps or equipment. A semisolid casting and forging method is provided in which a metal melt is teemed so that it is supercooled into a lower die in a press so controlled that the metal melt has a rate of solidification as desired, thereby preparing a semisolid slurry; an upper die is brought into contact with the semisolid slurry; and thereafter at least one of the upper and lower dies is moved relatively towards the other at a rate of movement between 0.1 and 1.5 m/sec, thereby compressing the semisolid slurry to mold it into a product. The semisolid slurry preferably has crystal grains of a grain size of 50 μm or less.

## Claims

### Claim 1

A semisolid melt casting and forging method, comprising:
teeming a metal melt into a cavity of a lower die, and
moving at least one of the lower and an upper die relatively towards the other at a rate of movement to perform molding of the metal melt in a semisolid state;
wherein said metal melt is formed into a slurry having grains of a grain size of not more than 50 μm throughout the slurry, and
wherein said molding is initiated at a lapse of time ranging between 0.1 second and 10 seconds following an instant at which the metal melt is teemed.

### Claim 2 (depends on 1)

A semisolid melt casting and forging method as set forth in claim 1 wherein said lapse of time between the instant at which the metal melt is teemed and the instant at which the molding is initiated is between 0.1 second and 5 seconds.

### Claim 3

A semisolid melt casting and forging method, comprising the steps of:
teeming a metal melt so that it is supercooled to be teemed into a lower die in a press so controlled that the metal melt has a rate of solidification as desired, so as to make a semisolid slurry having crystal grains of a grain size of not more than 50 μm throughout;
bringing at least an upper die into contact with the semisolid slurry; and thereafter
moving at least one of the upper and lower dies relatively towards the other at a rate of movement between 0.1 and 1.5 meter per second at least after an instant at which the upper die comes in contact with said semisolid slurry, thereby compressing said semisolid slurry to mold it into a product.

### Claim 4 (depends on 1)

A semisolid melt casting and forging method as set forth in claim 1, wherein the metal melt as it is teemed is of a temperature higher by 10 to 30° C. than its liquid phase or liquidus temperature.

### Claim 5 (depends on 1)

A semisolid melt casting and forging method as set forth in claim 1, wherein the metal melt is cooled passing through a liquidus curve at a rate of cooling of not less than 2° C. per second.

### Claim 6 (depends on 1)

A semisolid melt casting and forging method as set forth in claim 1, wherein said lower die is of a temperature of 200° C.±100° C.

### Claim 7 (depends on 1)

A semisolid melt casting and forging method as set forth in claim 1, wherein said upper die is of a temperature different from that of said lower die.

### Claim 8 (depends on 7)

A semisolid melt casting and forging method as set forth in claim 7, wherein the temperature of at least a portion of said upper die is lower than the temperature of said lower die.

### Claim 9 (depends on 1)

A semisolid melt casting and forging method as set forth in claim 1, wherein the ratio in mass of a product to a raw material is not less than 0.9.