Abstract
A method of producing flexible polypropylene fabric bags with heat fused seams comprising providing fabric pieces, wherein each fabric piece has a coated side and an uncoated side; positioning fabric pieces so that a coated side of one fabric piece faces a coated side of another fabric piece; selecting an area of fabric to be joined for forming a seam or joint; applying heat to the area to be joined that is less than the melting point of the fabrics, for forming one or more seams or joints and wherein the heat fused seams or joints of a resulting polypropylene bag retains at least 85% of the fabric strength without using sewing machines.
Claims37
A method of producing a flexible polypropylene fabric bulk bag, of the type that can hold 2,000 to 4,400 pounds of bulk material, with heat fused seams or joints that are stitch hole free, comprising:
- a. providing a plurality of highly oriented polypropylene woven fabric pieces, wherein at least one of said fabric pieces has a coated side with a bonding coating that has propylene elastomers, elastomers or combinations thereof and that is operable to form a seam or joint for the bag when melted, and wherein at least one of the fabric pieces has a coated side with a standard polypropylene fabric coating that is different from the bonding coating, the standard polypropylene fabric coating having a majority percentage of polypropylene and a small percentage of polyethylene;
- b. forming an overlapped area by positioning the at least one fabric piece that has the coated side with the bonding coating so that the bonding coating faces the standard polypropylene fabric coating on the at least one fabric piece having said standard polypropylene fabric coating;
- and
- c. applying heat and pressure to the overlapped area formed in step “b” to melt the bonding coating in the overlapped area and to form a bond between the bonding coating and the standard polypropylene fabric coating and a stitch hole free joint or seam for the bulk bag, wherein said bond has strength to maintain the said 2,000 to 4,400 pounds of bulk material within the bag without breaking and wherein the joint or seam has the following directly adjacent layers:
- (i) polypropylene fabric, (ii) bonding coating, (iii) standard coating;
- and (iv) polypropylene fabric;
- and
- d. forming one or more additional overlapped areas as desired between selected fabric pieces to be joined of the plurality of highly oriented polypropylene woven fabric pieces, and applying heat and pressure to the one or more additional overlapped areas to form one or more bonds between standard polypropylene fabric and bonding coatings to establish one or more additional stitch hole free bag joints.
5 more elements
A method of producing a flexible polypropylene fabric bulk bag of the type that can hold 2,000 to 4,400 pounds of bulk material, with heat fused seams that are stitch hole free in a single step, comprising:
- a. providing a folded top panel of flexible polypropylene fabric and a folded body panel of flexible polypropylene fabric, and overlapping the folded top panel and the folded body panel to provide 8 layers of flexible polypropylene fabric in an overlapped area that has:
- i. a top layer for the top panel, having a flat side;
- ii. a second layer for the body panel, having a flat side;
- iii. a third layer for the body panel, having a gusset side;
- iv. a fourth layer for the top panel, having a gusset side;
- v. a fifth layer for the top panel, having a gusset side;
- vi. a sixth layer for the body panel, having a gusset side;
- vii. a seventh layer for the body panel, having a flat side;
- and
- viii. an eighth layer, for the top panel having a flat side;
- b. wherein the layers of flexible polypropylene fabric have either a bonding coating having propylene-based plastomers, propylene-based elastomers, or a combination thereof, or a standard polypropylene fabric coating, which is different from the bonding coating and which has a majority percentage of polypropylene and some polyethylene;
- c. wherein in the overlapped area the layers of flexible polypropylene fabric are positioned so that all areas intended to be joined have said bonding coating facing said standard polypropylene fabric coating;
- d. centering the overlapped area under a seal bar;
- and
- e. applying heat below the melting point of the fabric and pressure in the overlapped area to the eight layers of flexible polypropylene fabric to form a bond between the bonding coating and the standard polypropylene fabric coating at the overlapped area to define a heat sealed seam or joint that is stitch hole free, and wherein the heat sealed seam of joint has the following directly adjacent four layers:
- (i) polypropylene fabric;
- (ii) bonding coating, (iii) standard polypropylene fabric coating, (iv) polypropylene fabric.
14 more elements
A method of automated production for producing a flexible polypropylene fabric bulk bag of the type that can hold 2,000 to 4,400 pounds of bulk material with heat fused joints that are stitch hole free, the method comprising steps of:
- a. providing layers of flexible polypropylene fabric, including tubular flexible polypropylene fabric layers, wherein some layers are gusseted and some layers are flat, and wherein the layers of flexible polypropylene fabric either comprise a bonding coating having propylene-based plastomers, propylene-based elastomers, or a combination thereof, or have a standard polypropylene fabric coating that is different from the bonding coating and has a majority percentage of polypropylene and small percentage of polyethylene;
- b. positioning the layers of flexible polypropylene fabric so that one layer of flexible polypropylene fabric overlaps another layer of flexible polypropylene fabric at one or more desired joint locations and so that a bonding coating on one of the layers of flexible polypropylene fabric faces a standard polypropylene fabric coating on another of the layers of flexible polypropylene fabric in the desired joint locations so that the one or more desired joint locations have the following directly adjacent layers:
- (i) polypropylene fabric, (ii) bonding coating, (iii) standard polypropylene fabric coating;
- and (iv) polypropylene fabric;
- and
- c. applying low heat to at least the melting point of the bonding coating and below the melting point of the fabric and low pressure to the joint locations to melt the bonding coating and to create a bond between said bonding coating and said standard polypropylene fabric coating in each joint location, each bond operable to maintain 2,000 to 4,400 pounds of bulk material within the bulk bag.
3 more elements
A method of making a bulk bag of the type that can hold 2,000 to 4,400 pounds of material by joining highly oriented polypropylene woven fabrics, including the following steps:
- a) coating polypropylene fabrics to be joined with materials, wherein at least one piece of polypropylene fabric to be joined is coated with a bonding coating having propylene-based plastomers, propylene-based elastomers or a combination thereof, the bonding coating having a melting point lower than a melting point of the polypropylene fabrics to be joined, and wherein at least one piece of polypropylene fabric to be joined is coated with a standard polypropylene fabric coating that is different from the bonding coating and which has a majority percentage of polypropylene and some polyethylene;
- b) positioning polypropylene fabrics to be joined so that the at least one piece of polypropylene fabric coated with the bonding coating faces the at least one piece of polypropylene fabric coated with the standard polypropylene fabric coating;
- c) heating the bonding coating to said bonding coating's melting point to melt said bonding coating;
- and
- d) applying pressure at least until the bonding coating forms a bond with the standard polypropylene fabric coating and a bag joint, and wherein the bond between the bonding coating and standard polypropylene fabric coating is operable to withstand pressure applied to the bag joint when the bulk bag is filled with 2,000 to 4,400 pounds of bulk material, and wherein the bag joint has the following directly adjacent four layers:
- (i) fabric, (ii) bonding coating, (iii) standard polypropylene fabric coating;
- and (iv) fabric.
4 more elements
A method of making a highly oriented polypropylene fabric bulk bag, of the type that can hold 2,000 to 4,400 pounds of bulk material, with heat fused and stitch hole free joints, the method comprising steps of:
- a. providing a highly oriented polypropylene fabric top having a top joint portion with a top standard coating that has a majority of polypropylene and some polyethylene at least in the top joint portion;
- b. providing a highly oriented polypropylene fabric body comprising upper and lower body joint portions with a body heat sealing coating at least in the upper and lower body joint portions, wherein the body heat sealing coating is different from the top standard coating, said body heat sealing coating made of propylene-based plastomers, elastomers, or combinations thereof;
- c. providing a highly oriented polypropylene fabric bottom comprising a bottom joint portion with a bottom standard coating that has a majority of polypropylene and some polyethylene at least in the bottom joint portion, and wherein the body heat sealing coating is also different from the bottom standard coating;
- d. forming a first heat fused joint providing an at least nearly air tight seal between the top and the body by overlapping the top joint portion with the body upper joint portion, and applying heat to at least a melting point of the body heat sealing coating, which is below a melting point of the fabrics, and pressure so that the body heat sealing coating melts and forms a first bond with the top standard coating, and wherein the first heat fused joint has the following directly adjacent four layers:
- top fabric, top standard coating, body heat sealing coating, body fabric;
- and
- e. forming a second heat fused joint providing an at least nearly air tight seal between the body and the bottom by overlapping the body lower joint portion and the bottom joint portion, and applying heat and pressure so that the body heat sealing coating melts and forms a second bond with the bottom standard coating, and wherein the second heat fused joint has the following directly adjacent four layers:
- body fabric, body heat sealing coating, bottom standard coating, bottom fabric.
5 more elements
A method of forming a highly oriented polypropylene fabric bulk bag, of the type that can hold 2,000 to 4,400 pounds of material, with heat fused seams, comprising:
- a. providing a top spout formed from a continuous piece of highly oriented polypropylene fabric including a first inner surface and a first outer surface, with a top spout unsealed upper portion and a top spout unsealed lower portion, the top spout having a first laminate coating that has a majority percentage of polypropylene and a smaller percentage of polyethylene on at least a portion of the first outer surface;
- b. providing a top formed from a piece of highly oriented polypropylene fabric and including a second inner surface and a second outer surface, with a top unsealed upper portion and a top unsealed lower portion, the top having a first bonding coating on at least a portion of the second inner surface, the first bonding coating being different from the first laminate coating and having propylene plastomers, elastomers, or combinations thereof;
- c. providing a body formed from a continuous piece of highly oriented polypropylene fabric having a third inner surface and a third outer surface with a body unsealed upper portion and a body unsealed lower portion, the body having a second laminate coating on at least a portion of the third outer surface, the second laminate coating having a majority percentage of polypropylene and a smaller percentage of polyethylene and being different from the first bonding coating;
- d. providing a bottom formed from a piece of highly oriented polypropylene fabric and including a fourth inner surface and a fourth outer surface with a bottom unsealed upper portion and a bottom unsealed lower portion, the bottom having a second bonding coating on at least a portion of the fourth inner surface, the second bonding coating being different from the second laminate coating and having propylene plastomers, elastomers, or combinations thereof;
- e. providing a bottom spout formed from a continuous piece of highly oriented polypropylene fabric and including a fifth inner surface and a fifth outer surface, a bottom spout unsealed upper portion and a bottom spout unsealed lower portion, the bottom spout having a third laminate coating on at least a portion of the fifth outer surface, the third laminate coating being different from the second bonding coating and having a majority percentage of polypropylene and a smaller percentage of polyethylene;
- f. forming a first overlapped area by overlapping the top spout unsealed lower portion and top unsealed upper portion so that the first laminate coating and first bonding coating face each other, and forming a first heat fused joint to connect the top spout and the top by applying heat and pressure to the first overlapped area to melt the first bonding coating and form a first bond between the first bonding coating and first laminate coating, and wherein the first heat fused joint has the following directly adjacent four layers:
- top spout fabric, first laminate coating, first bonding coating, and top fabric;
- g. forming a second overlapped area by overlapping the top unsealed lower portion and body unsealed upper portion so that the first bonding coating and second laminate coating face each other, and forming a second heat fused joint to connect the top and body by applying heat and pressure to melt the first bonding coating and form a second bond between the first bonding coating and second laminate coating, and wherein the second heat fused joint has the following directly adjacent four layers:
- (i) top fabric, (ii) first bonding coating, (iii) second laminate coating, and (iv) body fabric;
- h. forming a third overlapped area by overlapping the body unsealed lower portion and bottom unsealed upper portion so that the second laminate coating and second bonding coating face each other, and forming a third heat fused joint to connect the bottom and body by applying heat and pressure to melt the second bonding coating and form a third bond between the second bonding coating and second laminate coating, and wherein the third heat fused joint has the following directly adjacent four layers:
- (i) body fabric, (ii) second laminate coating, (iii) second bonding coating, and (iv) bottom fabric;
- and
- i. forming a fourth overlapped area by overlapping the bottom unsealed lower portion and bottom spout unsealed upper portion so that the second bonding coating and third laminate coating face each other, and forming a fourth heat fused joint by applying heat and pressure to melt the second bonding coating and form a fourth bond between the second bonding coating and third laminate coating, and wherein the fourth heat fused joint has the following directly adjacent four layers:
- (i) bottom fabric, (ii) second bonding coating, (iii) third laminate coating, and (iv) bottom spout fabric.
11 more elements