Abstract
An object of the present invention is to provide a lithium secondary battery that has a lithium nickel phosphate compound in the positive electrode, is free of collapse of the crystal structure even at high potentials and is resistant to cycle deterioration. The lithium secondary battery according to the present invention has a positive electrode active material. This positive electrode active material contains a lithium nickel phosphate compound that is represented by the general formula LiNi(1-x)MnxPO4 (wherein 0<x≤0.15) and that has an orthorhombic crystal structure belonging to space group Cmcm.
Claims7
A lithium secondary battery comprising a positive electrode active material,
- wherein the positive electrode active material contains a particle formed of a lithium nickel phosphate compound represented by the following general formula
- LiNi(1-x)MnxPO4 wherein 0.0001≤x≤0.01,
- at least a portion of the surface of the particle is coated with carbon, and
- the crystal structure of the lithium nickel phosphate compound is an orthorhombic crystal structure that has been controlled to space group Cmcm by a reducing action of the carbon.
A positive electrode active material for a lithium secondary battery, comprising a particle formed of a lithium nickel phosphate compound represented by the following general formula
- LiNi(1-x)MnxPO4 wherein 0.0001≤x≤0.01,
- wherein at least a portion of the surface of the particle is coated with carbon, and
- the crystal structure of the lithium nickel phosphate compound is an orthorhombic crystal structure that has been controlled to space group Cmcm by a reducing action of the carbon.
A method of producing a positive electrode active material for a lithium secondary battery, comprising:
- producing a starting material mixed solution by mixing, in a solvent, starting materials for a positive electrode active material formed of a lithium nickel phosphate compound represented by the following general formula
- LiNi(1-x)MnxPO4 wherein 0.0001≤x≤0.01
- the starting materials being prepared so as to provide a molar ratio between manganese (Mn) and nickel (Ni) of 0<Mn/(Ni+Mn)≤0.01;
- heating the starting material mixed solution to obtain a precipitate;
- pre-firing this precipitate to obtain a precursor;
- coating at least a portion of the particle surface in the precursor with carbon;
- and
- subjecting the carbon-coated precursor to a main firing in the temperature region of 600° C. to 900° C. in an inert gas atmosphere, and through a reducing action of the carbon, making the crystal structure of the lithium nickel phosphate compound an orthorhombic crystal structure composed of space group Cmcm.